Aluminium TIG wire containing 5% Silicon for welding Al / Si and Al / Mg / Si material. The medium strength weld metal has excellent resistance to hot cracking. Not suitable where good colour match is required after anodising. Melting range 570-630°C.

Aluminium TIG wire containing a nominal 4.9% Magnesium and 0.7% Manganese to produce a higher strength weld metal than the standard 5% Mg alloy.

Aluminium TIG wire containing 5% Magnesium for welding similar composition Al / Mg and Al / Mg / Si materials. The high strength weld metal has very good corrosion resistance in marine environments. Excellent colour match with material to be anodised. The most versatile and universally used aluminium filler material. Melting range 560-630°C.

Aluminium MIG wire containing 5% Silicon for welding Al / Si and Al / Mg / Si material. The medium strength weld metal has excellent resistance to hot cracking. Not suitable where good colour match is required after anodising. Melting range 570-630°C.

Aluminium MIG wire containing 5% Magnesium for welding similar composition Al-Mg and Al-Mg-Si materials. The high strength weld metal has very good corrosion resistance in marine environments. Excellent colour match with material to be anodised. The most versatile and universally used aluminium filler material. Melting range 560-630°C.

Aluminium MIG wire containing a nominal 4.9% Magnesium and 0.7% Manganese to produce a higher strength weld metal than the standard 5% Mg alloy.